DINITROL 500 1K humidity-curing and one component polyurethane 310ml

Characteristics:
DINITROL 500 1K is a humidity-curing and one component polyurethane for the direct-glazing of automotive glasses. The adhesive DINITROL 500 1K includes the following properties: • good adhesion on paints • low odour • excellent working characteristics • very good standing properties • short cut-off string • high elasticity • solvent and PVC free • OEM approved • ageing and weather resistant

Application:
The application of the DINITROL 500 1K is done by extrusion out of drums, pails, foil wrapes and cartridges. The use of this product is suitable only for experienced users. Pre-tests are recommended for special applications. Further information: The following publications are available on request: - Safety data sheet - DINOL pre-treatment chart

Storage:
Storage temperature between 0°C and 35ºC

Technical properties:
Chemical base: Polyurethane
Colour: black paste
Cure mechanism: Humidity-curing
Density (DIN 53217-4): approx. 1’200 kg/m³
Non-sag properties: very good
Application temperature: 10°C – 40°C (product)
Skin formation time1 : approx. 30 min.
Open time1 : approx. 25 min.
Rate of cure: approx. 3 − 4 mm / 24 h
Shore A hardness (DIN 53505): approx. 55
Tensile strength (DIN 53504): approx. 9 MPa
Elongation at break (DIN 53504): approx. 600%
Tear strength (DIN 53515): approx. 10 N/mm
Lab-shear-strength (DIN EN 1465): approx. 7 MPa
G-modulus (DIN 54451): approx. 1.3 MPa
Volume resistivity (DIN 60093): approx. 106 Ωcm
Glass transition temperature: approx. -40°C
Temperature resistants: Short term (approx. 1h) < 80°C < 120°C
Shelf life (storages below 25°C): cartridges / foil wrapes drums / pails 12 month 6 month
Safe-Drive-Away-Time1 : (FMVSS 212/208) without airbags: with passenger airbags: 2 hours 4 hours